Tensile
Strength |
Vickers
Hardness (F≥98N) |
Ball
Indentation Diameter |
Brinell
Hardness |
Rockwell
Hardness |
|
|---|---|---|---|---|---|
| N/mm² | HV | mm | HB | HRB | HRC |
| 0990 | 308 | 03.55 | 293 | ||
| 0995 | 310 | 03.54 | 295 | 31 | |
| 1000 | 311 | 03.53 | 296 | ||
| 1010 | 314 | 03.52 | 299 | ||
| 1020 | 317 | 03.50 | 301 | 32 | |
| 1030 | 320 | 03.49 | 304 | ||
| 1040 | 323 | 03.47 | 307 | ||
| 1050 | 327 | 03.45 | 311 | 33 | |
| 1060 | 330 | 03.44 | 314 | ||
| 1070 | 333 | 03.43 | 316 | ||
| 1080 | 336 | 03.41 | 319 | 34 | |
| 1090 | 339 | 03.40 | 322 | ||
| 1095 | 340 | 03.39 | 323 | ||
| 1100 | 342 | 03.38 | 325 | ||
| 1110 | 345 | 03.36 | 328 | 35 | |
| 1120 | 349 | 03.35 | 332 | ||
| 1125 | 350 | 03.34 | 333 | ||
| 1130 | 352 | 03.33 | 334 | ||
| 1140 | 355 | 03.32 | 337 | 36 | |
| 1150 | 358 | 03.31 | 340 | ||
| 1155 | 360 | 03.30 | 342 | ||
| 1160 | 361 | 03.29 | 343 | ||
| 1170 | 364 | 03.28 | 346 | 37 | |
| 1180 | 367 | 03.26 | 349 | ||
| 1190 | 370 | 03.25 | 352 | ||
| 1200 | 373 | 03.24 | 354 | 38 | |
| 1210 | 376 | 03.23 | 357 | ||
| 1220 | 380 | 03.21 | 361 | ||
| 1230 | 382 | 03.20 | 363 | 39 | |
| 1240 | 385 | 03.19 | 366 | ||
| 1250 | 388 | 03.18 | 369 | ||
| 1255 | 390 | 03.17 | 371 | ||
| 1260 | 392 | 372 | 40 | ||
| 1270 | 394 | 03.16 | 374 | ||
| 1280 | 397 | 03.14 | 377 | ||
| 1290 | 400 | 03.13 | 380 | ||
| 1300 | 403 | 03.12 | 383 | 41 | |
| 1310 | 407 | 03.10 | 387 | ||
| 1320 | 410 | 03.09 | 390 | ||
| 1330 | 413 | 03.08 | 393 | 42 | |
| 1340 | 417 | 03.07 | 396 | ||
| 1350 | 420 | 03.06 | 399 | ||
| 1360 | 423 | 03.05 | 402 | 43 | |
| 1370 | 426 | 03.04 | 405 | ||
| 1380 | 429 | 408 | |||
| 1385 | 430 | 03.02 | 409 | ||
| 1390 | 431 | 410 | |||
| 1400 | 434 | 03.01 | 413 | 44 | |
| 1410 | 437 | 03.00 | 415 | ||
| 1420 | 440 | 02.99 | 418 | ||