Tensile
Strength |
Vickers
Hardness (F≥98N) |
Ball
Indentation Diameter |
Brinell
Hardness |
Rockwell
Hardness |
|
|---|---|---|---|---|---|
| N/mm² | HV | mm | HB | HRB | HRC |
| 0200 | 063 | 07.32 | 060 | ||
| 0210 | 065 | 07.22 | 062 | ||
| 0220 | 069 | 07.04 | 066 | ||
| 0225 | 070 | 06.99 | 067 | ||
| 0230 | 072 | 06.95 | 068 | ||
| 0240 | 075 | 06.82 | 071 | ||
| 0250 | 079 | 06.67 | 075 | ||
| 0255 | 080 | 06.63 | 076 | ||
| 0260 | 082 | 06.56 | 078 | ||
| 0270 | 085 | 06.45 | 081 | 41.00 | |
| 0280 | 088 | 06.35 | 084 | 45.00 | |
| 0290 | 091 | 06.25 | 087 | 49.00 | |
| 0300 | 094 | 06.19 | 089 | 51.00 | |
| 0305 | 095 | 06.16 | 090 | 52.00 | |
| 0310 | 097 | 06.10 | 092 | 54.00 | |
| 0320 | 100 | 06.01 | 095 | 56.00 | |
| 0330 | 103 | 05.93 | 098 | 58.00 | |
| 0335 | 105 | 05.87 | 100 | 59.00 | |
| 0340 | 107 | 05.83 | 102 | 60.00 | |
| 0350 | 110 | 05.75 | 105 | 62.00 | |
| 0360 | 113 | 05.70 | 107 | 63.50 | |
| 0370 | 115 | 05.66 | 109 | 64.50 | |
| 0380 | 119 | 05.57 | 113 | 66.00 | |
| 0385 | 120 | 05.54 | 114 | 67.00 | |
| 0390 | 122 | 05.50 | 116 | 67.50 | |
| 0400 | 125 | 05.44 | 119 | 69.00 | |
| 0410 | 128 | 05.38 | 122 | 70.00 | |
| 0415 | 130 | 05.33 | 124 | 71.00 | |
| 0420 | 132 | 05.32 | 125 | 72.00 | |
| 0430 | 135 | 05.26 | 128 | 73.00 | |
| 0440 | 138 | 05.20 | 131 | 74.00 | |
| 0450 | 140 | 05.17 | 133 | 75.00 | |
| 0460 | 143 | 05.11 | 136 | 76.50 | |
| 0465 | 145 | 05.08 | 138 | 77.00 | |
| 0470 | 147 | 05.05 | 140 | 77.50 | |
| 0480 | 150 | 05.00 | 143 | 78.50 | |
| 0490 | 153 | 04.96 | 145 | 79.50 | |
| 0495 | 155 | 04.93 | 147 | 80.00 | |
| 0500 | 157 | 04.90 | 149 | 81.00 | |
| 0510 | 160 | 04.86 | 152 | 81.50 | |
| 0520 | 163 | 04.81 | 155 | 82.50 | |
| 0530 | 165 | 04.78 | 157 | 83.00 | |
| 0540 | 168 | 04.74 | 160 | 84.50 | |
| 0545 | 170 | 04.71 | 162 | 85.00 | |
| 0550 | 172 | 04.70 | 163 | 85.50 | |
| 0560 | 175 | 04.66 | 166 | 86.00 | |
| 0570 | 178 | 04.62 | 169 | 86.50 | |
| 0575 | 180 | 04.59 | 171 | 87.00 | |
| 0580 | 181 | 04.58 | 172 | ||
| 0590 | 184 | 04.54 | 175 | 88.00 | |